CNI design and manufacture of precision optical components and assemblies. As described in the customer solutions, we have strong capability to design and fabricate custom made optics with variously optical materials.
â—†Coated Laser Crystal
CNI is capable of supplying a large quantity of Laser crystals with high damage coatings to meet the tough requirement from both the OEM and R&D customers.
Crystals
Doping
Size(mm3)
Coating
Nd:YAG
An output coupler (OC) is a partially reflective mirror used in lasers to extract a portion of the laser beam from the optical resonator. Lasers operate by reflecting light between two or more mirrors which have an active laser medium between them. The medium amplifies the light by stimulated emission. For lasing to occur, the gain of the active medium must be larger than the total loss, which includes both unwanted effects such as absorption, and the intentional release of energy through the output coupler. In other words the laser must attain threshold.
ø4 mm, R=50/100/200 mm
Plano-Concave, HR946 nm, HT473nm
Plano-Concave, HR1064 nm, HT532nm
ø4 mm, R=50/200 mm
Plano-Concave, HR1342 nm, HT671nm
ø4 mm, R=50/100/200 mm
Plano-Concave, PR1064nm
Frequency Doubler or Second Harmonic Generation (SHG) is a special case of sum frequency generation if the two input wavelengths are the same. The simplest scheme for frequency doubling is extracavity doubling. The laser passes through the nonlinear crystal only once. However, if the power density of laser is low, focused beam, intracavity doubling and external resonant cavity are normally used to increase the power density on the crystals.
Crystals
LBO
2x2x5
2x2x5
2x2x5
AR@1064nm&532nm
2x2x5
2x2x5
2x2x5
Laser Crystal Laser Crystal,Laser Crystal Awards,Laser Engraved Crystal,Laser Cut Crystal Changchun New Industries Optoelectronics Technology Co., Ltd. , https://www.lasersciences.com
Fortunately, there are several parts of design such as hinges, fiber optic connector bases, and new style connectors are closely dependent on MIM technology. These products are being produced in a large number and MIM technology is being adopted by more and more.
MIM and CIM--Drome can provide one-stop service solution.
The basic attributes include:
1.Economical production of complex parts with weight from 0.03 to 200g from high-performance engineering materials.
2.Parts with high dimensional precision (±0.1%~±0.5%) and good surface quality (surface roughness 1~2μm).
3.Parts with high relative density (96%~100%), homogeneous microstructure and superior performance.
4.Adaptable to powders of various materials and wide application of the parts.
5.Material saving through the recycle of wastes, production process with high level of automation and suitable for mass production
Flow chart of metal injection molding
Application of MIM
Products Range:
Â
Material
Â
Typical Values
Â
Â
Designation Code
Density g/cm3
Tensile Properties
Young's modulus, Gpa
Un-notched Charpy Impact Energy,J
Hardness,Rockwell
Â
Â
UTS. Mpa
Y.S. (0.2%), Mpa
Elongation (in 25.4mm) %
Â
Â
Macro (apparent)
 Micro (converted)
MIM-Fe2Ni
7.8
280
115
25
Â
Â
55 HRB
50HRCÂ Â Â Â
MIM-Fe8Ni
7.8
450
Â
12
Â
Â
84HRB
50HRCÂ Â Â Â
MIM-2200 (as sintered)
7.8
290
125
40.0
190
135
45 HRB
Â
MIM-2700 (as sintered)
7.8
415
255
26.0
190
175
69 HRB
Â
MIM-4605 (as sintered)
7.8
440
205
15.0
200
70
62 HRB
Â
MIM-4605 (Q&T)
7.8
1655
1480
2.0
205
55
48 HRC
55 HRC
MIM-304L
7.8
500
Â
70
Â
Â
60 HRB
Â
MIM-316L (as sintered)
7.85
520
175
50.0
190
190
67 HRB
Â
MIM-410
7.7
900
Â
7
Â
Â
Â
40 HRC
MIM-420 (heat treated)
7.7
1380
1200
12
190
40
Â
45-60HRC
MIM-430L (as sintered)
7.8
410
240
25.0
210
150
65 HRB
Â
MIM-440C
7.8
700
590
15
Â
Â
Â
45-60HRC
MIM-17-4PH (as sintered)
7.8
900
730
6.0
190
140
27 HRC
Â
MIM-17-4PH (heat treated)
7.8
1190
1090
6.0
190
140
Crystals
Standard Product
Nd:YVO4
1%
3x3x2
Coated for 1064 nm, 532 nm, 1342 nm, 671 nm laser as required.
0.5%
3x3x5
1%
3x3x2
Coated for 1064 nm, 532 nm, 946 nm, 473 nm laser as required.
1%
3x3x23
â—†Output Coupler
Standard Product
Wavelength
Size
Goating
473 nm OC
532 nm OC
ø4 mm, R=50/100/200 mm
671 nm OC
1064 nm OC
â—†Frequency Doubling Crystal
Standard Product
Size(mm3
Coating
AR@1064nm&532nm/946nm&473nm/1342nm&671nm
KTP
BBO
AR@1064nm/532nm/266nm
Technics: MIM
Quoted Condition: 2D / 3D Drawing / Sample
Package: Carton, Plastic Bag, Export Package
OEM/ODM: Welcome
Production Time: 15-30 Days
Weight: 24.8g
Size: 102.5*10.4 mm
Trademark: drome
Transport Package: Carton
Specification: 290*190
Origin: Suzhou, China
MIM(Metal powder Injection Molding) isthe5th generation of metal forming technology. Over 40 years of development, people gradually find more applications for MIM process especially in the 3C products application. From initial groping to mature stage, MIM technology witness the ups and downs of 3C products in the past ten years.