• Model NO.: ER70S-6/DIN SG2/EN G3Si1
  • Material: Mild Steel
  • Extended Length: >20mm
  • Certificates: ABS CE ISO TUV Db Lr Gl BV Nk CCS RoHS etc
  • Business Type: Manufacture
  • Specification: CE ROHS
  • HS Code: 72292000
  • Type: Rolling Wire
  • Flux Containing: Not Containing Flux
  • Diameter: 0.8 0.9 1.0 1.2mm
  • OEM: Provided
  • Trademark: SOLID
  • Origin: Shandong
AWS ER70S-6/ DIN SG2

Description:
ER70S-6 is a kind of mild steel copper coated welding wire, suitable for 100% CO2 and Argon& CO2 mixed gas protective welding with stable feasibility, good welding seams, less spatters and excellent welding process properties.

Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1

Diameter; 0.8 0.9 1.0 1.2 1.6
Package: 5kg 15kg 20kg/spool, 100~350kg/drum
Spool type: Black/white plastic spool, metal spool
Certificates: ABS CE ISO TUV DB LR GL BV NK CCS ROHS

Application:
Used to weld ship building steel(A, B, D, E, A36, D36, E36)and equivalent mild steel or 550Mpa grade mild alloy steel, such as container building, construction machine, railway construction, pressure vessel for semi-auto or automatic gas shielded welding.

Factory introduction:

Established: Year 1996
Empolyee: Near 2000 person
Production: More than 3000 tons/month
Raw material: Qingsteel ER50-6E etc

C  Mn  Si  P  S  Ni  Cr  Cu
0.08  1.51  0.89  0.015  0.013  0.016  0.021  0.18
hemical composition of welding wire(%) C Mn Si P S Cr Ni Cu
0.06~0.15 1.40~1.85 0.80~1.15 ≤ 0.025 ≤ 0.035 - - ≤ 0.50
Mechanical Properties or Deposited Metal Yield strengthσ 0.2(Mpa) Tensile strengthσ b(Mpa) Elongationδ 5(%) AKV impact(J)
≥ 420 ≥ 500 ≥ 22 ≥ 27(-29)
 
Wire Size(mm) φ 0.8 φ 1.0 φ 1.2 φ 1.6
Welding current(A) 40~140 50~220 80~350 120~550
Please be noted Wire shall be stocked in dry. open the packs just when welding to avoid the wire rust.
Before welding please clean out the oil, rust, water etc from the work parts

Parallel co-rotating twin-screw extruders are used as mixing equipment. In the processing of high molecular weight materials, the modification process and the preparation of polyolefin materials and engineering plastic masterbatches need to be fully and thoroughly mixed, depending on the material system. Excellent equipment performance, reasonable mixing technology, advanced combination technology and rich processing experience are the key factors that determine the success and efficiency of the mixture.

Lab Double Screw Extruder

Lab Extruder,Lab Double Screw Extruder,Lab Twin Screw Extruder,Laboratory Twin Screw Extruder

Nanjing Juli Chemical Machinery Co., Ltd. , https://www.jlextruder.com